ENFLEX EA3575A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ENPLAST Americas, a Ravago Group Company |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wi4ySU_ENFLEX-EA3575A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 75 Shore A TPE (Styrenic Block Copolymer based) for injection molding and extrusion applications. This grade offers soft/tactile feel and adhesion (overmolding) to Nylon. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 10 seconds, extruded | 71 | ASTM D2240 | |
| Shore A, 10 seconds, injection molding | 75 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.69 | MPa | ASTM D412 |
| Tensile Strength (Break) | 6.03 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | 35.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 27 | % | ASTM D395B |
| 70°C, 22 hr | 48 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -52.0 | °C | ASTM D746 |
| Dynamic Service Temperature | 90 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 171 - 199 | °C | |
| Middle Temperature | 229 - 241 | °C | |
| Front Temperature | 241 - 249 | °C | |
| Nozzle Temperature | 221 - 241 | °C | |
| Processing (Melt) Temp | 229 - 249 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Injection Pressure | 5.17 - 8.96 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm | |
| Clamp Tonnage | 3.4 - 4.8 | kN/cm² | |
| Cushion | 5.08 - 12.7 | mm |
| Injection instructions |
|---|
| Holding Time: 5 to 7 Sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 160 - 179 | °C | |
| Cylinder Zone 1 Temp. | 229 - 241 | °C | |
| Cylinder Zone 3 Temp. | 241 - 249 | °C | |
| Cylinder Zone 5 Temp. | 241 - 249 | °C | |
| Adapter Temperature | 229 - 249 | °C | |
| Melt Temperature | 229 - 249 | °C | |
| Die Temperature | 229 - 249 | °C |
| Extrusion instructions |
|---|
| Screw: L/D 20:1 or greater (L/D 24:1 preferred)Cooling Water: 60 - 85°F (15-30°C)Screw Speed: 100 - 200 rpmScreen Pack: 20/40/60 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1035 E | ROMIRA GmbH | PC+ABS | Romiloy® |
| RTP 1302 | RTP Company | PPS | RTP |
| Tenac™-C ZLD75 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Tarnoform® 500 GF2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| KOPA® KN333G30 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |