Versaflex™ HC MT224
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wfWmqF_Versaflex-HC-MT224.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Versaflex™HC MT224 is a transparent high-performance TPE material, converted to medical catheter research and development. VersaflexTM HC MT224 adopts a special formula and does not use any plasticizer. New Products. Commercial norms have not yet been established. • Flexible • Special formula without plasticizer • High transparency |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 75 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (21°C, 1900 µm) | 470 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 23°C 2 | 3.23 | MPa | ASTM D412 |
| 300% strain, 23°C 3 | 5.33 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 9.38 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 530 | % | ASTM D412 |
| Compression Set | ASTM D395B | ||
| 22°C, 22 hr | 19 | % | ASTM D395B |
| 45°C, 22 hr | 52 | % | ASTM D395B |
| 70°C, 22 hr | 70 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | ASTM D3835 | ||
| 200°C, 1340 sec^-1 | 176 | Pa·s | ASTM D3835 |
| 200°C, 11200 sec^-1 | 36.0 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C | |
| Die Temperature | 171 - 199 | °C |
| Extrusion instructions |
|---|
| Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC MT224. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Drying is not RequiredRear: 330F-370FCenter: 350F-400FFront: 360F-420FScrew: 100-500RPM |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | Mouth die c |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P med | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| BMC 6241 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CP PRYME® Polyethylene PE100LD-8M | Chase Plastics Services Inc. | LDPE | CP PRYME® Polyethylene |
| Kingfa JH710 G10 | Kingfa | PC Alloy | Kingfa |
| Sylvin 8980-70LG Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |