HiFill FR® ABS GF30 FR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | web6PR_HiFill-FR-ABS-GF30-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill FR® ABS GF30 FR is an Acrylonitrile Butadiene Styrene (ABS) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 112 | °C | |
| 1.8 MPa, Unannealed | 103 | °C | |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 210 to 227 | °C | |
| Middle Temperature | 216 to 232 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Nozzle Temperature | 193 to 216 | °C | |
| Processing (Melt) Temp | 227 to 254 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-4/35 NAT | Techmer Engineered Solutions | Nylon 612 | TES |
| FHR Polypropylene AP5206-HN | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Flontech® FT-M02-2 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Plaskon 3400F-14 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| NORYL PPX™ PPX830 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |