Borcoat™ BB108E-1199
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borcoat™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | weGguG_Borcoat-BB108E-1199.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borcoat BB108E-1199, a ready made white compound, is a high molecular weight, low melt flow rate polypropylene block copolymer. As a top-coat in three component polypropylene systems, Borcoat BB108E-1199 fulfils the requirements in NFA 49-711, DIN 30678, Shell specification (DEP 31.40.30.31) and Pr EN10286 when used in combination with Borcoat BB125 or Borcoat BB127E and compatible powder epoxy and applied under sound processing conditions. Borcoat BB108E-1199 is used in steel pipe coating as a top-coat for three component systems, UV stabilized, highly protected against thermal ageing, and designed for continuous use at high temperatures 110°C on-shore and up to 140°C for very specific off-shore projects. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ISO 1183 | ||
| -- 1 | 0.900 | g/cm³ | ISO 1183 |
| -- 2 | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 3(Injection Molded) | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 25 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 145 | °C | ISO 306/A |
| Additional Information |
|---|
| Fungia Resistance, ASTM G21: No GrowthBacteria Resistance, ASTM G21: No Growth |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 220 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Cylinder Zone 5 Temp. | 200 - 220 | °C | |
| Melt Temperature | 220 - 240 | °C | |
| Die Temperature | 210 - 220 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 210 to 220°C |
| Note Message | |
|---|---|
| 1 . | Base Resin |
| 2 . | Compound |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LS01018 - C | Premier Polymers, LLC. | LLDPE | Premier |
| SLOVASTER® B1 HML GF 10 | Plastcom | PBT | SLOVASTER® |
| INLUBE POMHTF13 | Infinity LTL Engineered Compounds | Acetal (POM) Homopolymer | INLUBE |
| Lifoflex® UV FLAM 60600 | Müller Kunststoffe GmbH | TPE | Lifoflex® |
| LEXAN™ VR2220 resin | SABIC Innovative Plastics | PC | LEXAN™ |