ASTALOY™ PC/ABS A800LG
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wdHc3Y_ASTALOY-PC-ABS-A800LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS A800LG is a low gloss general purpose alloy of ABS and Polycarbonate and is designed for standard injection moulding applications requiring a low gloss finish, balance of high impact toughness, product rigidity, high heat resistance and mouldability. Typical applications include automotive interior components, seat belt surround, fascia panels and air vent mouldings. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS A800LGU ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/3.8 kg | 4.0 | g/10 min | |
| 260°C/5.0 kg | 12 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 480 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 60.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 105 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 112 | °C | |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 245 to 265 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SP-0170 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Amodel® A-4160 HSL | Solvay Specialty Polymers | PPA | Amodel® |
| Elastron® G P.G401.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| PERCOM® XG1128 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| Polygen SG6R | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |