Network Polymers LDPE 10 1010 EVA
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wcNwkp_Network-Polymers-LDPE-10-1010-EVA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers LDPE 10 1010 EVA is an Ethylene Vinyl Acetate Copolymer (EVA) product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (Natural) | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) 1(190°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 10.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 23°C, 3.18 mm, Injection Molded | 95 | ||
| Shore D, 23°C, 3.18 mm, Injection Molded | 45 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break, 23°C, 3.18 mm, Injection Molded) | 12.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm, Injection Molded) | 660 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (3.18 mm) | 110 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -77.2 | °C | ASTM D746 |
| Vicat Softening Temperature | 77.2 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HO-20T | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Spartech Polycom 3030-10004 | Spartech Polycom | PVC Alloy | Spartech |
| Biffa r-PP Black | Biffa Polymers Ltd | PP, Unspecified | Biffa |
| EPO-TEK® H61LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| MAJORIS HG264 - 1298 | AD majoris | PP, Unspecified | MAJORIS |