Alathon® H6017
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wc9SGC_Alathon-H6017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H6017 provides good processing characteristics and exhibits excellent toughness and color as well as low odor and good molded-part stability. Typical applications include housewares, caps, closures and various food containers. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Spiral Flow | 28.2 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1000 | MPa | |
| 1% Secant | 868 | MPa | |
| Tensile Strength 2(Break) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1470 | MPa | |
| 1% Secant | 1370 | MPa | |
| 2% Secant | 1120 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 550 | J/m | ASTM D4218 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Peak Melting Temperature | 116 to 133 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 757A | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Aquivion® E98-15S | Solvay Specialty Polymers | PFSA | Aquivion® |
| Delrin® 311DP NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Elastron® G G500.A30.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Lytex 9063FR | Quantum Composites Inc. | Epoxy | Lytex |