Capran® 980
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Capran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wc8DFw_Capran-980.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CAPRAN® 980 is a clear (low haze level), heat-stabilized cast film produced from modified nylon 6 resin. It is recommended as bagging film for advanced composite fabrication and other high temperature applications where dimensional stability, adherence to sealant tapes and uniform film gauge are essential. CAPRAN® 980 has excellent heat stability and resistance to pinholing. It can be used at temperatures up to 390oF (199oC) for typical composite cure cycle times. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Secant Modulus - MD (51 µm) | 552 | MPa | ASTM D882 |
| Tensile Strength - MD | ASTM D882 | ||
| Yield, 51 µm | 31.0 | MPa | ASTM D882 |
| Break, 51 µm | 112 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break, 51 µm) | 380 | % | ASTM D882 |
| Elmendorf Tear Strength - MD (51 µm) | 130 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 218 - 220 | °C | ASTM D3418 |
| Additional Information |
|---|
| Dimensional Stability, ASTM D1204, 30 mins, 300°F: <2% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecolen® CP20 GR20 NL XC30 | Eurotec Engineering Plastics | PP Copolymer | Tecolen® |
| Hifax TKC 243X 3001 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Lumid® GP2200A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| Sylvin 8356-73 Brown 7437 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sumiliteresin® PR-55438 | SBHPP | Phenolic | Sumiliteresin® |