KMI PP KM840-K6M5P
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | KMI PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wbEVxT_KMIPPKM840K6M5P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KM840-K6M50 is a clarified polypropylene random copolymer. Applications: Consumer and healthcare products |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 | % | ASTM D638 |
| Flexural Modulus - Tangent | 1050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | > 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 83.9 | °C | ASTM D648 |
| Peak Melting Temperature | 145 - 152 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (635 µm) | 6.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3399 X 117884 D | RTP Company | PVDF | RTP |
| Iupilon® EFR3000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Iupiace® AH91 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LUVOCOM® 1850-8628 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| MARPOL® COPP 35.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |