Karina IVORY PVC COMPOUND -E 655-35/1-F-IS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wY46R6_Karina-IVORY-PVC-COMPOUND--E-655-35-1-F-IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Karina IVORY PVC COMPOUND -E 655-35/1-F-IS is a Polyvinyl Chloride product. It is available in Latin America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.39 to 1.45 | g/cm³ | ASTM D792 |
| Color | OK | ME 12 | |
| Color a | 0.660 to 3.66 | ME 12 | |
| Color b | 12.4 to 15.4 | ME 12 | |
| Color L | 80.0 to 83.0 | ME 12 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 63 to 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 8.83 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 200 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 8.83 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 200 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® ESd 420 V | Quadrant Engineering Plastic Products | PEI | Quadrant EPP |
| RTP 701 CC | RTP Company | HDPE | RTP |
| VECTRA® A130 | Celanese Corporation | LCP | VECTRA® |
| DURANEX® 315NFK | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Sumiliteresin® PR-NR-1 FI | SBHPP | Phenolic | Sumiliteresin® |