FARBOSET® 5000
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Cosmic Plastics, Inc. |
| Trademark: | FARBOSET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wXIpL1_FARBOSET-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cosmic FARBOSET 5000 Black is a mineral and glass filled epoxy molding compound featuring fast cure rates, low abrasion and excellent hot strength. It is designed for the encapsulation of coils, transformers, switches and other electrical components requiring good hot rigidity in molding. It's low abrasion characteristics makes 5000 especially suited for the encapsulation of solenoid valves. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.88 | g/cm³ | |
| Apparent Density 1 | 1.00 | g/cm³ | |
| Spiral Flow | 66.0 | cm | |
| Molding Shrinkage - Flow | 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | |
| Flexural Modulus | 13400 | MPa | |
| Flexural Strength | 114 | MPa | |
| Compressive Strength | 283 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact | 16 | J/m |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 150 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.7E-5 | cm/cm/°C | |
| -- 3 | 7.9E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.67 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | |
| Volume Resistivity | > 5.0E+16 | ohms·cm | |
| Dielectric Strength 4(3.18 mm) | > 16 | kV/mm | |
| Dielectric Constant (1 kHz) | 4.50 | ||
| Dissipation Factor (1 kHz) | 7.0E-3 | ||
| Arc Resistance | 180 | sec |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 5 | |||
| 5°C | 52 | wk | |
| 25°C | 1.0 | wk | |
| 35°C | 0.29 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Loss Factor - 1 kHz | 0.0320 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (150°C) | 0.017 to 0.050 | hr | |
| Gel Time 6 | 0.50 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 150 to 180 | °C | |
| Injection Pressure | 0.345 to 6.89 | MPa |
| Note Message | |
|---|---|
| 1 . | Powder |
| 2 . | Alpha 1 |
| 3 . | Alpha 2 |
| 4 . | Method A (Short-Time) |
| 5 . | Defined as not more than 40% loss of spiral flow based on original values. |
| 6 . | 150°C/1000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPOA10400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| CP PRYME® Polypropylene PPC100NB-10M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| EcoBlend® HCL7110NH | Shanghai KumhoSunny Plastics Co., Ltd. | PLA+PMMA | EcoBlend® |
| Hyundai EP PA66 LD900 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Pibiter® HI C3311 NERO900 | SO.F.TER. SPA | PBT | Pibiter® HI |