P-BLEND X6
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | P-BLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wTvk5Y_P-BLEND-X6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS with good impact strength and heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.75 - 0.85 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 22 | kJ/m² | ISO 180 |
| 23°C | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 107 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 128 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 50 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 255 - 275 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4007 UP | RTP Company | PPA | RTP |
| TAIRIPRO S1803 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| APEX® 84842 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina WHITE PVC COMPOUD -E 836-10/132-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ KAL22 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |