Thermx® CG033
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Thermx® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wSzChq_Thermx-CG033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermx® CG033 is a 30% glass fiber reinforced polycyclohexylenedimethylene terephthalate for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 270 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 262 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 105 | °C | ISO 11357-2 |
| Melting Temperature 2 | 283 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.2E-5 | cm/cm/°C | |
| Transverse | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 560 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density of Melt | 1.420 | g/cm³ | Internal Method |
| Ejection Temperature | 220 | °C | Internal Method |
| Specific Heat Capacity of Melt | 1470 | J/kg/°C | Internal Method |
| Thermal Conductivity of Melt | 0.20 | W/m/K | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 295 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8207-80FU White 1483 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Abstron MIF45EP | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Boda BDT40CP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| LNP™ THERMOCOMP™ LX04015 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |
| Kepex® 3930GFU | Korea Engineering Plastics Co., Ltd | PBT+ASA | Kepex® |