KIBILAC® PW-997S
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBILAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wSib4b_KIBILAC-PW-997S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KIBILAC® PW-997S is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 3.80 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 48.0 | MPa | ISO 527-2/50 |
| Break | 42.0 | MPa | ISO 527-2/50 |
| 3.18 mm 1 | 44.1 | MPa | ASTM D638 |
| Tensile Strain (Break) | 80 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1800 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 3 | 64.7 | MPa | ASTM D790 |
| -- 4 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 390 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 250 | J/m | ASTM D256 |
| -- | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm 5 | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 6.35 mm 6 | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525, ISO 306/A50 7 7 |
| -- | 108 | °C | ISO 306/A120 |
| -- | 92.0 | °C | ISO 306/B50 |
| -- | 95.0 | °C | ISO 306/B120 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 93 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 200 to 220 | °C | |
| Cylinder Zone 3 Temp. | 220 to 250 | °C | |
| Cylinder Zone 5 Temp. | 230 to 260 | °C | |
| Die Temperature | 210 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 120°C/hr |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom E65595 | Spartech Polycom | PVC, Unspecified | Spartech |
| Sylvin 8299-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEXUS ABS ABSLG3030 | Nexus Resin Group, LLC. | ABS | NEXUS ABS |
| Braskem PP RP 340S | Braskem | PP Random Copolymer | Braskem PP |
| Axiall PVC 11860 | Axiall Corporation | PVC, Flexible | Axiall PVC |