TAISOX 2410
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wRSU6G_TAISOX-2410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2410 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific. The processing method is: blow molding film or co-extrusion molding. The main features of TAISOX 2410 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 265 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 343 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 12.7 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 13.7 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 41.2 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 32.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 760 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 180 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 210 | g | ASTM D1922 |
| TD : 38 µm, blown film | 870 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature | 123 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 35 | ASTM D2457 | |
| Clarity | 50.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 23 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 360E4861312 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| TUFLIN™ HS-7029 NT 7 | The Dow Chemical Company | LLDPE | TUFLIN™ |
| ALCOM® PA6 900/1 GF8 GB7 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Hax™ HFX 505/2 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| POCAN® B 4235 Z 000000 | LANXESS Corporation | PBT | POCAN® |