SABIC® LLDPE 318B
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wRKku6_SABICLLDPE318B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description 318B is Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures used during production of Cast films. Films produced using this resin gives excellent optical properties, good puncture resistance and tear strength. Typical Applications Cling film, Stretch films for manual and pellet wrap, melt embossed films and other general purpose applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 30 µm | 135 | MPa | ASTM D882 |
| TD : 30 µm | 140 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 13.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm | 10.0 | MPa | ASTM D882 |
| MD : Break, 30 µm | 28.0 | MPa | ASTM D882 |
| TD : Break, 30 µm | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 470 | % | ASTM D882 |
| TD : Break, 30 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 75 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 65 | g | ASTM D1922 |
| TD : 30 µm | 300 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm) | 90 | ASTM D2457 | |
| Haze (30.0 µm) | 5.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (30.0 µm) | 570 | J/cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 - 300 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HIP-372 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SABIC® PPcompound 9135 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Selvol™ 310 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| ADMER™ QF551A | Mitsui Chemicals America, Inc. | PP, Unspecified | ADMER™ |
| Fainplast PVC PH 55 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |