LNP™ THERMOCOMP™ RF002ES compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wQuZzb_LNP-THERMOCOMP-RF002ES-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF002ES is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1002 EM HS Product reorder name: RF002ES |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.89 | % | ISO 294-4 |
| Flow : 24 hr | 0.77 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 1.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4850 | MPa | ASTM D638 |
| -- | 5130 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 87.8 | MPa | ASTM D638 |
| Break | 90.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 2.3 | % | ISO 527-2 |
| Break | 2.5 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4610 | MPa | ASTM D790 |
| -- | 4280 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 156 | MPa | ASTM D790 |
| -- | 131 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 3 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.65 | J | ASTM D3763 |
| -- | 1.32 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 173 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 175 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 SI | RTP Company | PC | RTP |
| SABIC® PPcompound 5310 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Tecnoflon® FOR 537 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| ELASTOSIL® R plus 573/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Sylvin 8299-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |