Surlyn® 9910
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wQ1nhO_Surlyn-9910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Surlyn® 9910 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 9910 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238, ISO 1133 |
| Ion Type | Zinc |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - NBS Index | 610 | ASTM D1630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | |||
| -- | 46 | °C | ASTM D3418 |
| -- | 46 | °C | ISO 3146 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C, Compression Molded 1 | 13.8 | MPa | ASTM D638 |
| Break, 23°C | 24.8 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 290 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | ASTM D790 | ||
| -20°C | 731 | MPa | |
| 23°C | 330 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 360 | J/m | ASTM D256 |
| Tensile Impact Strength | ASTM D1822 | ||
| -40°C | 1010 | kJ/m² | |
| 23°C | 1020 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -105 | °C | ASTM D746 |
| Vicat Softening Temperature | 62.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 86.0 | °C | ASTM D3418, ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (6350 µm) | 6.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 185 to 285 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIVIC® 2100 | SIDIAC | NBR | SIVIC® |
| HiFill® PA6 0135 BL069 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ STAT-KON™ PX93058 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| Plexiglas® Frosted V045-68177 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 8280-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |