Mecoline IS RDX 1218 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wPqGYE_Mecoline-IS-RDX-1218-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The RDX 20521 compound is very low temperature resistant to -40°C and IRM 902 & IRM 903 oil resistant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (175°C/21.6 kg) | 7.0 | g/10 min | ISO 1133 |
| pH | > 4.5 | IEC 60754-2 | |
| Shrinkage - 1h at 120°C | < 2.0 | % | IEC 811-1-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test - penetration 4h at 140°C | < 50 | % | DIN VDE 0472 |
| Hot Set 1 | IEC 540 | ||
| Elongation under load | < 40 | % | |
| Residual elongation | < 10 | % | |
| Temperature Index | 300 | °C | ASTM D2863 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 4.00 | µS/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | % | IEC 754-1 |
| Toxicity | 2.00 | EN 50305 | |
| Vertical Burn Test | < 540 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 160 to 170 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 85 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 2 | > 12.0 | MPa | |
| -- 3 | > 9.00 | MPa | |
| Tensile Strain | |||
| Break 4 | > 180 | % | IEC 811-1-1 |
| Break 5 | > 200 | % | IEC 811-1-1 |
| Break, -40°C | > 35 | % | IEC 811-1-4 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (120°C, 240 hr) | < 25 | % | IEC 811-1-2 |
| Change in Tensile Strain at Break in Air (120°C, 240 hr) | < 25 | % | IEC 811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 40 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 130 to 140 | °C | |
| Cylinder Zone 2 Temp. | 150 to 160 | °C | |
| Cylinder Zone 3 Temp. | 160 to 170 | °C | |
| Cylinder Zone 4 Temp. | 160 to 170 | °C | |
| Cylinder Zone 5 Temp. | 160 to 170 | °C | |
| Adapter Temperature | 160 to 170 | °C | |
| Die Temperature | 160 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | at 200°C/15min/0.2 MPa |
| 2 . | After crosslinking |
| 3 . | Before crosslinking |
| 4 . | After crosslinking |
| 5 . | Before crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 CC GB 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| NYCOA Polyamide 5201 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Dynaprene® VER8500 | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Elastron® D P.D100.A50.B | Elastron USA, Inc. | SBS | Elastron® D |
| Plexiglas® Satinice df22 7H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |