TOPAS® 9506F-500
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | TOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wOoKru_TOPAS-9506F-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Film Grade, Improved moldability |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.00 | cm³/10min | |
| 230°C/2.16 kg | 6.00 | cm³/10min | |
| Water Absorption (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1A/1 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 1700 | MPa | |
| TD | 1700 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break | 50.0 | MPa | |
| TD : Break | 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 3.1 | % | |
| TD : Break | 3.1 | % | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.090 | g·mm/m²/atm/24 hr | ISO 15106-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | 65.0 | °C | ISO 11357-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend庐 UT3907 | Covestro - Polycarbonates | PC+PBT | Makroblend® |
| POLYSTONE® Marine-Tec | Röchling Engineering Plastics SE & Co. KG | TP, Unspecified | POLYSTONE® |
| NEXT REGRIND POMC M90-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Gallonprene® GP420-5503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hanwha Total PP BB110 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |