LNP™ STAT-KON™ Lexan_LCF1506 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wOaEi9_LNPSTATKONLexanLCF1506compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON LEXAN_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.050 - 0.15 | % | Internal method |
| Transverse flow : 3.20mm | 0.20 - 0.30 | % | Internal method |
| K (wear) Factor 1 | 1000 | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 2 | 10 | msec | FTMS 101B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 111 | MPa | ASTM D638 |
| Fracture | 111 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 50.0mm span 5 | 9080 | MPa | ASTM D790 |
| 100mm span 6 | 8420 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Fracture, 50.0mm span 7 | 161 | MPa | ASTM D790 |
| Fracture, 100mm span 8 | 154 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.19 | ASTM D1894 | |
| With steel-static | 0.41 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 280 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 11.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 142 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 144 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 139 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 277 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 288 - 316 | °C | |
| Nozzle Temperature | 288 - 316 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | 5000V to <50V |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Diamond PC 1008 N, 1008 NC | Network Polymers, Inc. | PC | Diamond PC |
| LNP™ STAT-KON™ MD000IS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |
| O'Tech OW 827 | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Kepital® TS-25HN | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| StarPrene® 6101-87 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPrene® |