Eltex® PF6612KE

Category:	mLLDPE , Metallocene Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wMUD1d_Eltex-PF6612KE.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® PF6612KE is a metallocene LLDPE grade produced in Europe.

Benefits & Features
Eltex® PF6612KE is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:

High impact strength and rigidity

Excellent optical properties

Very good bubble stability and extrudability, evene at low gauge and narrow die gap

Low temperature sealing characteristics

Eltex® PF6612KE is formulated with antioxidants, slip and antiblocking agents, and a processing aid. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance.

Applications
Eltex® PF6612KE has been developed for use in collation shrinkwrap, food packaging, refuse sacks and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6612KE offers easy extrudability.

General Information
Additive	Antiblock (300 ppm) 2 Antioxidant Erucamide Slip (1000 ppm)
Features	Antiblocking Antioxidant Good Processability High Impact Resistance High Rigidity Low Temperature Heat Sealability Opticals Slip
Uses	Film Food Packaging Packaging Shrink Wrap
Processing Method	Blown Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.927	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	< 0.30		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Modulus			ISO 527-3
1% Secant, MD : 25 µm, Blown Film	230	MPa
1% Secant, TD : 25 µm, Blown Film	270	MPa
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, Blown Film	13.0	MPa
TD : Yield, 25 µm, Blown Film	13.0	MPa
MD : Break, 25 µm, Blown Film	55.0	MPa
TD : Break, 25 µm, Blown Film	50.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 25 µm, Blown Film	570	%
TD : Break, 25 µm, Blown Film	690	%
Dart Drop Impact (25 µm, Blown Film)	200	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, Blown Film	160	g
TD : 25 µm, Blown Film	560	g

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature ¹	120	°C	ASTM D3418

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	65		ASTM D2457
Haze (25.0 µm, Blown Film)	7.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 230	°C

Note Message
1 .	2nd heating

Resin Grade	Manufacturer	Category	Trademark
RTP 1899 A X 106999	RTP Company	PC+Acrylic	RTP
Bapolene® 222B	Bamberger Polymers, Inc.	LDPE	Bapolene®
Geon™ Vinyl Wire & Cable WR7400L	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Wire & Cable
Hifax CA10GC	LyondellBasell Industries	TPO (POE)	Hifax
LUVOCOM® 1105-8135/GN	Lehmann & Voss & Co.	PEEK	LUVOCOM®