Elastollan® 1175AW
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wKpt5e_Elastollan-1175AW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 1175AW is a polyether-based thermoplastic polyurethane (TPU) containing a plasticizer. It contains a non-halogenated flame retardant and is rated UL-94 V-0 in vertical flame test for wall thicknesses of 0.9 mm - 1.1 mm, UL-94 V-2 for wall thicknesses of 1.2 mm and 3.0 mm. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1175AW is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 20 to 50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 8.96 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 10.3 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 20.0 | mg | ASTM D1044 |
| Abrasion - DIN | 45 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 60 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.72 | MPa | |
| 300% Strain | 17.9 | MPa | |
| Tensile Strength | 26.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength 1 | 80.6 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -48.0 | °C | Internal Method |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| 0.900 mm | V-0 | ||
| 1.10 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Norpex® PPE AX30GF | Custom Resins Group | PPE | Norpex® |
| Braskem PE SLL5405S | Braskem America Inc. | LLDPE | Braskem PE |
| Ferro PP LPP20BA09NA | Ferro Corporation | PP Copolymer | Ferro PP |
| HiFill® ABS 0167 | Techmer Engineered Solutions | ABS | HiFill® |
| POLYCOMPO PE 102 | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |