SAMAT 5003N2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | POLYROCKS CHEMICAL CO., LTD |
| Trademark: | SAMAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wKkeXT_SAMAT-5003N2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAMAT™ 5003N (+) are halogen-free environmental polypropylene (PP) with phosphorus and nitrogen as the flame retardant elements. The synergistic effect of coagulation phase and gas phase on flame retardation enhances the flame retardant efficiency, and the catalytic mechanism accelerates the melting and dropping of the system. The flammability can reach UL94-V2 (0.75mm,1.5mm and 3.0mm) and pass the water immersion test at 70°C for 168hrs (UL746C) and GWIT 750°C and GWFI 960°. They have the characteristics of low density of finished products, low smoke and little corrosion to molds. 5003N (+) pass UL tests and meet the requirements of RoHS, SVHC, PFOS&PFOA, 16P, Halogen-free and PAHs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Flexural Strength | 33.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 200 | J/m | ASTM D256 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | UL 746C, UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Flammability after water-boiling testing at 70°C for 168 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PC SP930 | Shuman Plastics, Inc. | PC | Shuman PC |
| Karina BLACK PVC COMPOUND -E 600-48/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucofin® 1412-t3 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Sylvin 8870-70D White 1502 | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| POTICON NTB935 | Otsuka Chemical Co., Ltd. | Nylon, Unspecified | POTICON |