TOLEN R030 BM
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | SIBUR, LLC |
| Trademark: | TOLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wKYCfr_TOLEN-R030-BM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP R030 BM is a propylene-ethylene random copolymer. The product features lower than average fluidity, and a special stabilization package containing a complex of additives that ensure necessary physical, mechanical properties and application performance of final products. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 23.0 | MPa | Internal Method |
| Tensile Strain 2(Yield) | 12 | % | Internal Method |
| Flexural Modulus 3 | 1000 | MPa | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | Internal Method |
| Vicat Softening Temperature | 135 | °C | Internal Method 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | A (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHM7005 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Tufpet PBT G2630 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Vydyne® R535J NT0665 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| EVERLON® TC-55C | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Polybutene-1 DP8510M | LyondellBasell Industries | PB | Polybutene-1 |