Order Products : sales@su-jiao.com
Generic ABS+PBT
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wIx0QL_Generic-ABS-PBT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PBT This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.08 - 1.32 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 7.0 - 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.64 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 104 - 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 36.5 - 51.7 | MPa | ASTM D638 |
| Yield, 23°C | 37.6 - 45.2 | MPa | ISO 527-2 |
| 23°C | 31.1 - 47.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 - 100 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 1630 - 2550 | MPa | ASTM D790 |
| 23°C | 1300 - 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 51.1 - 75.7 | MPa | ASTM D790 |
| 23°C | 59.8 - 70.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 83 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 30 - 660 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 92.4 - 150 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 77.0 - 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 84.9 - 90.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 64.4 - 80.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 8.4E+15 - 1.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 27 - 31 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 84.0 - 112 | °C | |
| Drying Time | 3.5 - 5.1 | hr | |
| Rear Temperature | 200 - 255 | °C | |
| Middle Temperature | 230 - 251 | °C | |
| Front Temperature | 245 - 251 | °C | |
| Nozzle Temperature | 239 - 241 | °C | |
| Processing (Melt) Temp | 230 - 255 | °C | |
| Mold Temperature | 59.4 - 70.6 | °C | |
| Back Pressure | 0.150 - 12.5 | MPa | |
| Screw Speed | 55 - 90 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PBTThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP563T | HMC Polymers | PP, Unspecified | Moplen |
| Network Polymers PP PPB 25 0802 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Formolene® 3320B | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| HONES® PPS HS-G40-5 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| EPALINE 354D55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |