Radilon® S URV600L 100 NAT 4154
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wHfFDs_Radilon-S-URV600L-100-NAT-4154.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 60% glass fiber reinforced injection moulding grade. Very high flowability. Natural colour. Suitable for parts requiring very high stiffness and high mechanical resistance, as in case of metal replacement applications. ISO 1043 : PA6 GF60 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.69 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 4.4 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 21400 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 255 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.1 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 19300 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 90 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/Af |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 650 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66G33UTL-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| TEREZ PA 6 7500 GF 50 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Unipren® Elastomers B3 PRTA010 70A EG06S1 UP341 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Varcum 29217R | Durez Corporation | Phenolic | Varcum |
| Hostacom M2 N14 | LyondellBasell Industries | PP Copolymer | Hostacom |