Order Products : sales@su-jiao.com
LNP™ VERTON™ UX03320 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wGmCb0_LNP-VERTON-UX03320-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON UX03320 is a compound based on Polyphthalamide resin containing proprietary fillers. Added feature of this grade is: Structural. Also known as: LNP* VERTON* Compound PDX-U-03320 Product reorder name: UX03320 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.050 to 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.080 to 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.15 | % | ISO 294-4 |
| Flow : 24 hr | 0.060 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Spiral Flow Length | Internal Method | ||
| 1.00 mm | 30.0 | ||
| 3.00 mm | 70.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 18200 | MPa | ASTM D638 |
| -- | 20300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 220 | MPa | ASTM D638 |
| Break | 200 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 18000 | MPa | ASTM D790 |
| -- 2 | 17700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 300 | MPa | ASTM D790 |
| -- | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| 23°C 4 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.0 | J | ASTM D3763 |
| -- | 19.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 275 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 to 327 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 24480 | Teknor Apex Company | TPV | Sarlink® TPV |
| Witcom PA6 2011/200 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| NEXT REPROCESSED ABS 6500-300R | NEXT Specialty Resins, Inc. | ABS | NEXT REPROCESSED |
| Sylvin 9067-90 Grey 9202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ LUX9612G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |