GLAMIDE® T-602G30
| Category: | PARA , Polyarylamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wEvpxi_GLAMIDE-T-602G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE® T-602G30 is a Polyarylamide (PARA) product filled with 30% glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 22 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 to 0.40 | -- | % | |
| 3.00 mm | 0.40 to 0.70 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.80 | -- | % | |
| Equilibrium, 65% RH | 1.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 260 | 235 | MPa | |
| Yield, 23°C | 190 | 115 | MPa | |
| Yield, 80°C | 100 | 72.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 3.6 | 4.2 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 10000 | 9200 | MPa | |
| 23°C | 8500 | 4000 | MPa | |
| 80°C | 4000 | 3200 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 260 | 250 | MPa | |
| Yield, 23°C | 230 | 120 | MPa | |
| Yield, 80°C | 140 | 95.0 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 65 | 80 | J/m | |
| 23°C | 130 | 210 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 217 | -- | °C | |
| 1.8 MPa, Unannealed | 205 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | 17 | kV/mm | ASTM D149 |
| Arc Resistance | 100 | 90.0 | sec | ASTM D495 |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 to 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Caltex PP M720 | GS Caltex | PP Impact Copolymer | Caltex PP |
| EPT 8120E | Mitsui Chemicals, Inc. | EPDM | EPT |
| Karina YELLOW PVC COMPOUND 830-02/277-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTP ZE-2601 Al2O3/GF 30% | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| Elastoskin® Lite 50555-05R Resin / S50555T Isocyanate | BASF Corporation | PUR, Unspecified | Elastoskin® |