ATTANE™ SL 4100G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wEeIbK_ATTANE-SL-4100G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™SL 4100G ultra-low density polyethylene resin is used to produce blown films. This type of film requires comprehensive excellent optical properties, excellent tear strength and impact strength, and excellent sealing performance. The product also has excellent flexural cracking resistance. Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.912 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 40 µm | 120 | MPa | ISO 527-3 |
| 2% secant, TD : 40 µm | 135 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 6.50 | MPa | ISO 527-3 |
| TD : Yield, 40 µm | 6.20 | MPa | ISO 527-3 |
| MD : Break, 40 µm | 31.0 | MPa | ISO 527-3 |
| TD : Break, 40 µm | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 640 | % | ISO 527-3 |
| TD : Break, 40 µm | 760 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 850 | g | ISO 7765-1/B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm | 690 | g | ASTM D1922 |
| TD : 40 µm | 850 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 3 | 92.0 | °C | ASTM D1525 |
| Melting Temperature 4 | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 40.0 µm) | 75 | ASTM D2457 | |
| Haze (40.0 µm) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜挤出的制造条件： 模具间隙 1.6 至 2.5 mm 熔体温度：190 至 240°C（理想值：215-225°C） 放大比：1.5 比 3.5 建议的厚度范围：10 至 80 µm |
| Note Message | |
|---|---|
| 1 . | Compression molded sample |
| 2 . | Compression molded sample |
| 3 . | Compression molded sample |
| 4 . | Compression molded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Minlon® 73M40 NC010 | DuPont Performance Polymers | Nylon 6 | Minlon® |
| RheTech Polypropylene RCC220-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Synthos PS GP 154 | Synthos S.A. | PS (GPPS) | Synthos PS |
| Larton GK/400 | LATI S.p.A. | PPS | Larton |
| Petlon R-Prime PET Clear 100 FR-36 | Petlon Polymers Ltd | PET | Petlon R-Prime |