LNP™ THERMOCOMP™ 2X95787 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wDgPnA_LNP-THERMOCOMP-2X95787-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2X95787 is a compound based on ETFE Copolymer resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-FP-E-95787 Product reorder name: 2X95787 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.83 | g/cm³ | ISO 1183 |
| -- | 1.84 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.8 | % | |
| Across Flow : 24 hr | 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 42700 | MPa | ASTM D638 |
| -- | 4050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Break | 45.5 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.3 | % | ASTM D638 |
| Yield | 8.6 | % | ISO 527-2 |
| Break | 14 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 33800 | MPa | ASTM D790 |
| -- | 4000 | MPa | ISO 178 |
| Flexural Stress | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 480 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 3 | 83 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 19.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 203 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 107 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 91.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 | °C | |
| Mold Temperature | 93.3 to 121 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polycarbonate PC300RUV | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Hanwha Total PP HJ400 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| Hapflex™ 596-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Karina CLEAR PVC COMPOUND -E 80/278-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1700-1401 | Lehmann & Voss & Co. | PPE | LUVOCOM® |