Novamid® 1013C5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Novamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wCL6x8_Novamid-1013C5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novamid® 1013C5 is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific for injection molding. Primary attribute of Novamid® 1013C5: Good Processability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 1.1 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.8 | -- | % | ISO 62 |
| Viscosity Number | 138 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | -- | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | -- | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 19 | -- | % | ISO 527-2 |
| Flexural Modulus | 2800 | -- | MPa | ISO 178 |
| Flexural Stress | 110 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 169 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 76.0 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 26 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.00 | -- | ||
| 1 MHz | 4.00 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.011 | -- | ||
| 1 MHz | 0.022 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Provista™ Copolyester | Eastman Chemical Company | Copolyester | Provista™ |
| Spartech Polycom PP6110F B5 | Spartech Polycom | PP, Unspecified | Spartech |
| TAROBLEND 66 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| MAJORIS DFR210 | AD majoris | PP, Unspecified | MAJORIS |
| TECHNYL® C 216 V15 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |