PLEXIGLAS® Tube XT
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | PLEXIGLAS® Tube |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wBap1r_PLEXIGLAS-Tube-XT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLEXIGLAS® XT rods and tubes are the clearest extruded tubes on the market today delivering brilliant quality, superior performance, and durability. PLEXIGLAS® XT rods and tubes are characterized by their flawless optics, and perfectly smooth surface free of striations. PLEXIGLAS® GS tubes are produced in the cast rotation process. Cast rods and square rods are made of casted semi-finished products. All cast forms have polished surfaces. Applications Due to the above characteristics PLEXIGLAS® rods and tubes are ideally suitable for.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water absorption- 24 h, 23°C 1 | 38.0 | mg | ISO 62 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold bending- Minimum radius | 330 x thickness | ||
| Maximum Service Temperature | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Smoke Gas Corrosiveness | None | ||
| Smoke Gas Volume | Very Low | DIN 4102 | |
| Smoke Toxicity | None | DIN 53436 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance | Yes |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ignition Point | 430 | °C | DIN 51794 |
| Surface Temperature - IR-radiator | °C | ||
| Weight Gain - during immersion 2 | % | ISO 62 | |
| Forming Temperature | |||
| -- | 150 - 160 | °C | |
| Reverse | > 80 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress 3 | ISO 527-2/5 | ||
| -40°C | 110 | MPa | ISO 527-2/5 |
| 23°C | 72.0 | MPa | ISO 527-2/5 |
| 70°C | 35.0 | MPa | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1fU |
| Notched Izod Impact | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ISO 306/B |
| CLTE - Flow (0 to 50°C) | 7.0E-5 | cm/cm/°C | DIN 53752-A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 92.0 | % | DIN 5036 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowing : <0.5% (DIN 5036) Reflection loss in the visible range (for each surface) : 4% Absorption in visible range : <0.05% |
| Note Message | |
|---|---|
| 1 . | Method 1, specimen 60 x 60 x 2mm³ |
| 2 . | Method 1 |
| 3 . | Type 1B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® D (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Armlen® PP TM 25.1 | Poly Plastic | PP, Unspecified | Armlen® |
| Flontech® FT-M02-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hypel® PEHD.3/.955 | Entec Polymers | HDPE | Hypel® |
| TABOREN® PC 22 B 70 | SILON s.r.o. | PP Copolymer | TABOREN® |