Bergadur™ BR3300-8025 RS NC012

Category: PBT , Polybutylene Terephthalate
Manufacturer: PolyOne Corporation
Trademark: Bergadur™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: wBO7lW_Bergadur-BR3300-8025-RS-NC012.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
20% glass fiber reinforced PBT
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 20% filler by weight
Appearance
  • Natural color
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.42g/cm³ASTM D792
Molding Shrinkage 0.50 - 1.0%ISO 294-4
MechanicalNominal ValueUnitTest Method
Tensile Strength 1110MPaASTM D638
Flexural Modulus 26050MPaASTM D790
Flexural Strength 3195MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (23°C, 3.20 mm)90J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm)200°CASTM D648
ElectricalNominal ValueUnitTest Method
Surface Resistivity 1.0E+15ohmsASTM D257
FlammabilityNominal ValueUnitTest Method
Flame Rating (1.60 mm)HBInternal method
InjectionNominal ValueUnit
Drying Temperature 110 - 130°C
Drying Time 4.0 - 6.0hr
Rear Temperature 240 - 270°C
Middle Temperature 240 - 270°C
Front Temperature 240 - 270°C
Mold Temperature 75.0 - 95.0°C
Injection instructions
Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW
Note Message
1 .5.0 mm/min
2 .1.3 mm/min
3 .1.3 mm/min
Resin Grade Manufacturer Category Trademark
Promyde® B30 P2 G20 NUREL, S.A. Nylon 6 Promyde®
TABOND 3047 SILON s.ro LLDPE TABOND
Torelina® A504FG1 Toray Resin Company PPS Torelina®
DOW™ HDPE 05962B The Dow Chemical Company HDPE DOW™ HDPE
Epiall® 1904B-1 Sumitomo Bakelite North America, Inc. Epoxy Epiall®