RELENE® O19010
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wAyzE6_RELENE-O19010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| O19010 is an octene comonomer based Linear Low Density Polyethylene (LLDPE), with optimum levels of antioxidant, antiblocking agent, slip additive and polymer processing aid. The grade is designed to make blown film for ehavy duty applications and liquid packaging, where excellent seal through contamination, toughness, impact strength and tear resistance are desired. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Blown Film | 0.12 | ||
| vs. Itself - Static, Blown Film | 0.20 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 12.5 | MPa | |
| TD : Yield, 40 µm, Blown Film | 13.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 35.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 650 | % | |
| TD : Break, 40 µm, Blown Film | 800 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 280 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, Blown Film | 550 | g | |
| TD : 40 µm, Blown Film | 1100 | g |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 40.0 µm, Blown Film) | 80 | ASTM D523 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME POLYPROPYLENE 10% TALC V2 | RIALTI Srl | PP Homopolymer | RIALFLAME |
| RECANYL AB36BK9502 | Jackdaw Polymers | Nylon 66 | RECANYL |
| Scolefin 52 G 13-0 | Ravago Group | PP Homopolymer | Scolefin |
| AIE PA66 6010ST | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Kynar® 8600 | Arkema | Plastics Additive, Other | Kynar® |