Eltex® PF6012AA

Category:	mLLDPE , Metallocene Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	w9dTGL_Eltex-PF6012AA.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® PF6012AA is a metallocene LLDPE resin produced in Europe.

Benefits and Features
Eltex® PF6012AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:

Very low sealing initiation temperature

Excellent Hot Tack strength, particularly advantageous for HFFS packaging lines

Unrivalled impact strength and puncture resistance

Very good bubble stability and extrudability similar to the best LLDPE blown film grades

Properties ideally balanced in machine and transverse directions

Excellent blending compatibility with other LLDPE and LDPE grades

Applications
Eltex® PF6012AA has been developed for use in highly technical film like food packaging, lamination and co-extrusion applications where superior mechanical and sealing performance is required. In addition Eltex® PF6012AA offers easy extrudability. Eltex® PF6012AA is particularly suitable for multilayer film applications where it can be used neat or as a blending partner with LLDPE or LDPE in sealing layers.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Hexene Comonomer Low Temperature Heat Sealability Puncture Resistant Ultra High Impact Resistance
Uses	Blending Film Food Packaging Laminates Packaging Sealing Devices
Processing Method	Blown Film Coextrusion Extrusion Laminating

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.912	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Modulus			ISO 527-3
1% Secant, MD : 25 µm, Blown Film	120	MPa
1% Secant, TD : 25 µm, Blown Film	130	MPa
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, Blown Film	8.00	MPa
TD : Yield, 25 µm, Blown Film	8.00	MPa
MD : Break, 25 µm, Blown Film	73.0	MPa
TD : Break, 25 µm, Blown Film	69.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 25 µm, Blown Film	520	%
TD : Break, 25 µm, Blown Film	620	%
Dart Drop Impact (25 µm, Blown Film)	> 2000	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, Blown Film	180	g
TD : 25 µm, Blown Film	350	g

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	97.0 to 114	°C	Internal Method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	83		ASTM D2457
Haze (25.0 µm, Blown Film)	3.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 230	°C

Resin Grade	Manufacturer	Category	Trademark
Maxelast® C4915	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
WaterClear Ultra 10122	DSM Somos®	Unspecified	WaterClear
DynaMix™ 2044-15GF	Polymer Dynamix	Nylon 66	DynaMix™
PENTAMID B L5 R H schwarz	PENTAC Polymer GmbH	Nylon 6	PENTAMID B
OTECH ALLOY XLO9141 - Riser Jacket	OTECH Corporation	TP, Unspecified	OTECH ALLOY