Order Products : sales@su-jiao.com
RTP ESD C 1500-50D
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8ptuu_RTP-ESD-C-1500-50D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 to 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 276 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 13.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 207 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 6.89 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | No Break | ASTM D256 | |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 40.6 | °C | |
| 1.8 MPa, Unannealed | 121 | °C | |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 188 to 216 | °C | |
| Middle Temperature | 188 to 216 | °C | |
| Front Temperature | 188 to 216 | °C | |
| Mold Temperature | 21.1 to 37.8 | °C | |
| Injection Pressure | 34.5 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LMA332 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Wah Hong BMC BUG-3101C Electrical | Wah Hong Industrial Corp. | TS, Unspecified | Wah Hong BMC |
| DOMAMID® 6G20V0EF | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| INEOS PP H14A-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| LUVOCOM® 80-8604/EM/BL | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |