VECTRA® E488i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8RLf1_VECTRA-E488i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultra low warp |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.43 | % | ISO 294-4 |
| Flow direction | 0.14 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 5.0E-3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 54 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | MPa | ISO 178 |
| Compressive Modulus | 11000 | MPa | ISO 604 |
| Flexural Strain at Break | 1.8 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 29 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 55 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.24 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.045 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.150 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 335 - 345 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 340 - 355 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Zone 4 Temperature: 340 to 360°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 CC HI HB | RTP Company | PP, Unspecified | RTP |
| Shin-Etsu Elastomer KE-561U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Tarnamid® T-30 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Lupolen 3721 C | LyondellBasell Industries | MDPE | Lupolen |
| Polifor® 12 TR/40 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |