LNP™ STAT-KON™ DD0009E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8H2uM_LNP-STAT-KON-DD0009E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DD0009E is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant, Easy Molding. Also known as: LNP* STAT-KON* Compound D-EM FR Product reorder name: DD0009E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3060 | MPa | ASTM D638 |
| -- | 3060 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.2 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/5 |
| Break 3 | 61.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 4 | 3.8 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2/5 |
| Break 5 | 4.1 | % | ASTM D638 |
| Break | 8.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3060 | MPa | ASTM D790 |
| -- 7 | 2890 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 52 | J/m | ASTM D256 |
| 23°C 9 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2000 | J/m | ASTM D4812 |
| 23°C 10 | 100 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.7 | J | ASTM D3763 |
| -- | 5.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 128 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.0E-6 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ 100V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Catalyst CT/2-LR UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Cri-Line IF-615-65 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| DJSilicone NE-9170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| ISOTHANE® 3080A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |