Moplen EP341T

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Moplen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	w7HNV8_Moplen-EP341T.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LyondellBasell Australia's polypropylene grade EP341T is an ultra high flow impact copolymer with a modified molecular weight distribution and is formulated with a general-purpose additive package. EP341T also contains nucleation additives. EP341T is designed for injection moulding applications requiring very easy mould filling, low warpage, and good impact/rigidity balance. End use products typically made from EP341T include thin walled containers and refrigerator packaging ware.

General Information
Additive	Nucleating agent
Features	Nucleated Low warpage Impact copolymer Impact resistance, good Good formability High liquidity Compliance of Food Exposure Medium hardness
Uses	Packaging Thin wall container Container
Agency Ratings	AS 2070-1999 FDA 21 CFR 176.170(c), Table 2, Cond. C FDA 21 CFR 176.170(c), Table 2, Cond. D FDA 21 CFR 176.170(c), Table 2, Cond. E FDA 21 CFR 176.170(c), Table 2, Cond. F FDA 21 CFR 176.170(c), Table 2, Cond. G FDA 21 CFR 176.170(c), Table 2, Cond. H FDA 21 CFR 177.1520(a) 3 (i) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	60	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	71		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	22.0	MPa	ISO 527-2
Flexural Modulus	1100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ISO 180/1A
-20°C	2.0	kJ/m²	ISO 180/1A
0°C	2.5	kJ/m²	ISO 180/1A
23°C	3.5	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	75.0	°C	ISO 75-2/B
1.8 MPa, not annealed	50.0	°C	ISO 75-2/A
Vicat Softening Temperature	145	°C	ISO 306/A

Additional Information
Falling Weight Impact Strength @ -40°C, BS2782-306b: 8 J

Resin Grade	Manufacturer	Category	Trademark
T-Blend® 4801B-SP	TSRC Corporation	SBS	T-Blend®
Nipol® AR 14	Zeon Corporation	Rubber	Nipol® AR
Axiall PVC 1901 Clear 7002	Axiall Corporation	PVC, Flexible	Axiall PVC
Generic PEI	Generic	PEI	Generic
Hostacom X 678/1 LS71	LyondellBasell Industries	PP Copolymer	Hostacom