Greenflex® FD 20 F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w6tNfH_Greenflex-FD-20-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FD 20 F is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Films produced by Greenflex FD20 exhibit good optical properties, high impact resistance, tensile strength, elongation at break and low creep. Main Application Greenflex FD 20 F is recommended for thermo-shrinkable films and multilayer stretch films for food packaging, included deep-frozen food packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 5.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 95 | ||
| Shore D, Injection Molded | 44 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 120 | MPa | |
| 1% Secant, TD : Blown Film | 125 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 8.00 | MPa | |
| TD : Yield, Blown Film | 8.00 | MPa | |
| MD : Break, Blown Film | 26.0 | MPa | |
| TD : Break, Blown Film | 26.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 450 | % | |
| TD : Break, Blown Film | 600 | % | |
| Dart Drop Impact 1(Blown Film) | 420 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 26.0 | kN/m | |
| TD | 40.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 85.0 | °C | ISO 306/A |
| Melting Temperature | 104 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 80 | ASTM D2457 | |
| Haze (Blown Film) | 1.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9665-35 Clear Blue 1836 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Ultraform® N 2520 L | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Network Polymers LLDPE 11 2024 | Network Polymers, Inc. | LLDPE | Network Polymers LLDPE |
| EnviroPro 9003 | West Michigan Compounding | PP Copolymer | EnviroPro |
| LNP™ THERMOCOMP™ JF006 compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |