LNP™ THERMOCOMP™ 2Z004 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w6bz0R_LNP-THERMOCOMP-2Z004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2Z004 is a compound based on ETFE resin containing 20% Milled Glass. Also known as: LNP* THERMOCOMP* Compound FP-EF-1004 M Product reorder name: 2Z004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.84 | g/cm³ | |
| -- | 1.83 | g/cm³ | |
| Water Absorption (24 hr, 50% RH) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1710 | MPa | ASTM D638 |
| -- | 1520 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 29.0 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2/5 |
| Break 3 | 21.0 | MPa | ASTM D638 |
| Break | 22.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 23 | % | ASTM D638 |
| Yield | 22 | % | ISO 527-2/5 |
| Break 5 | 53 | % | ASTM D638 |
| Break | 78 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1280 | MPa | ASTM D790 |
| -- 7 | 1220 | MPa | ISO 178 |
| Flexural Stress | 24.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 620 | J/m | ASTM D256 |
| 23°C 8 | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 9 | 120 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 26.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 89.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 52.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 50.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 2500-WH10 | Prime PVC® | PVC, Rigid | Prime |
| Radilon® A ERV130LK 333 NER 5025 | Radici Plastics | Nylon 66 | Radilon® |
| Aegis® H73ZP | Honeywell | Nylon 6 | Aegis® |
| LNP™ THERMOTUF™ IX02582 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOTUF™ |
| Sylvin 8600-85 Yellow 4173 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |