MonoSol® AF L337
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w5MvAB_MonoSol-AF-L337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF L337 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L337 is a highly plasticized grade of PVOH cold water-soluble packaging film with good film to film tack and is the film choice for stretch wrapping applications. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 7.6 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 50.0 µm | 24.0 | sec | |
| Disintegration : 24°C, 50.0 µm | 12.0 | sec | |
| Dissolution : 10°C, 50.0 µm | 83.0 | sec | |
| Dissolution : 24°C, 50.0 µm | 58.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (50.0 µm) | 16.1 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 60 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 50 µm | 49.6 | MPa | |
| 100%, MD : 50 µm | 17.2 | MPa | |
| 10%, TD : 50 µm | 43.4 | MPa | |
| 100%, TD : 50 µm | 8.96 | MPa | |
| Tensile Strength | |||
| MD : Break, 50 µm | 30.3 | MPa | ASTM D882 |
| TD : Break, 50 µm | 31.7 | MPa | ASTM D882 |
| MD : 50 µm | 30.3 | MPa | ISO 527-3 |
| TD : 50 µm | 31.7 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Break, 50 µm | 230 | % | ASTM D882, ISO 527-3 |
| TD : Break, 5.0E-3 µm | 420 | % | ASTM D882 |
| TD : Break, 50 µm | 420 | % | ISO 527-3 |
| Elmendorf Tear Strength | |||
| MD : 50 µm | 1300 | g | ASTM D1922 |
| TD : 50 µm | 1500 | g | ASTM D1922 |
| MD : 50 µm | 0.13 | N | ISO 6383-2 |
| TD : 50 µm | 0.15 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP WPP2194-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| NEXT REPROCESSED POMC M90-300R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| Multi-Flex® TPE A9002 MR | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Lotader® 3410 | Arkema | EBA | Lotader® |
| Lumid® LW4403A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |