MAJORIS AT367
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w4T3rL_MAJORIS-AT367.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AT367 is a filled talc reinforced, high molecular weight, low melt index flow rate polypropylene block copolymer with a very high stiffness at a good level of impact strength and UV stabilised . APPLICATIONS AT367 is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3090 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 28.2 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.4 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.7 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 75.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Head Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AESN G9 T6L | Arkema | Nylon 12 | Rilsan® |
| Delrin® 300TE BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Karina BLACK COLOR CONCENTRATE 48/1-FC-6 (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pibifor® 34S5301NC 0001 | SO.F.TER. SPA | PBT | Pibifor® |
| Rotuba CAB B902 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |