Aarolene® ARPS 100-3
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Aaron Industries Corp. |
| Trademark: | Aarolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w3QD78_Aarolene-ARPS-100-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A Reprocessed High Impact polystyrene resin compounded black specifically designed for high speed injection molding applications. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 27.6 | MPa | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 73.9 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN JHC-371 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SANREX S10G32 | Techno Polymer Co, Ltd. | SAN | SANREX |
| Titalon® 3200CF | Titan Plastics Compounds Co., Ltd. | Nylon 12 | Titalon® |
| Fiberfil® J-60/20 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| LNP™ THERMOCOMP™ 2X95787 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |