Susteel® P-42-11
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | TOSOH Corporation |
| Trademark: | Susteel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w3OHU2_Susteel-P-42-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This grade is specialized in capacitor cap. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.91 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.40 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (Equilibrium) | < 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 98.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 12800 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Tensile Weld Strength | 54.0 | MPa | ASTM D638 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length (1.00 mm) | 8.00 | cm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 260 | °C | ASTM D648 |
| Melting Temperature | 285 | °C | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 175 | V | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 290 to 330 | °C | |
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 to 20.0 | MPa | |
| Screw Speed | 100 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA612G43-BK10 | Pier One Polymers, Inc. | Nylon 612 | MAXAMID™ |
| VESTAMID® D DX9321 | Evonik Industries AG | Nylon 612 | VESTAMID® D |
| Chemlon® 543 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Durethan® BKV 15 H3.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| IROGRAN® A 85 E 4607 E | Huntsman Corporation | TPU-Polyester | IROGRAN® |