LNP™ THERMOCOMP™ 2C004 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w2HwVC_LNP-THERMOCOMP-2C004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2C004 is a compound based on ETFE resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-EC-1004 Product reorder name: 2C004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.75 | g/cm³ | ASTM D792 |
| -- | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.65 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13300 | MPa | ASTM D638 |
| -- | 12200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 60.2 | MPa | ASTM D638 |
| Fracture | 59.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.5 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10500 | MPa | ASTM D790 |
| -- | 10600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 107 | MPa | ASTM D790 |
| -- | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.0 | J | ASTM D3763 |
| -- | 6.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 246 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 209 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 187 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M80063 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| VITAMIDE® BR15 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| WELNEX™ RFX4V | Japan Polychem Corporation | PP Random Copolymer | WELNEX™ |
| AIE PC/ABS 12G4F | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| SQUARE® SR8658A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |