| PA 6, 30 % glass fibers, injection molding, improved flowability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 0.58 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.14 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 0.23 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.050 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 190 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 9020 | 5530 | MPa | ASTM D638 |
| 23°C | 9300 | 5700 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 174 | 97.2 | MPa | ASTM D638 |
| Break, 23°C | 180 | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Break, 23°C | 3.2 | 5.6 | % | ASTM D638 |
| Break, 23°C | 3.0 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 7800 | 5100 | MPa | ASTM D790 |
| 23°C 5 | 8400 | 6000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 270 | 170 | MPa | ASTM D790 |
| 3.5% Strain, 23°C | 250 | 155 | MPa | ISO 178/A |
| 23°C 6 | 265 | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 5.3 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 10-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 45 | kJ/m² | |
| 23°C | 65 | 85 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -40°C | 45 | 40 | kJ/m² | |
| 23°C | 60 | 80 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 2.80 | -- | J | |
| 23°C | 2.90 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 797 | -- | N | |
| 23°C | 813 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 150 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOSINT® 2155 natural color | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| YUPLENE® R151A | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Next Nylon 66 Prime Series PGHS33-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Boda BDF-KK2801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Fenochem T 5800 | Chemiplastica, Inc. | Phenolic | Fenochem |