Kynar Flex® 2851-00
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w1axNn_Kynar-Flex-2851-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 2850-00 is a pelletized, semi-crystalline VF2 based copolymer. The powder form of this resin is designated KYNAR FLEX® 2851-00. KYNAR FLEX® 2850-00 has been specifically designed for use in wire and cable constructions which require an Underwriters Laboratories temperature of 150°C. It is close in physical performance to KYNAR® PVDF homopolymer grades, but has a higher flexibility. KYNAR FLEX® 2850-00 is also used in chemical applications as extruded sheet and pipe liners. ADDITIONAL CHARACTERISTICS: Excellent thermal stability Excellent abrasion resistance Excellent purity and chemical resistance Impervious to UV degradation Self extinguishing material Extremely low smoke emission characteristics Pigmentable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.80 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 70 to 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 31.0 to 41.4 | MPa | |
| Break, 23°C | 27.6 to 48.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 30 to 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1030 to 1240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 20.7 to 34.5 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 41.4 to 58.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 155 to 160 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 2300 to 2700 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1025 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sinvicomp SFC8201 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sindustris PP M1501 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Chemical Resources PMMA1200 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| GELOY™ EXGY0070 resin | SABIC Innovative Plastics | ASA | GELOY™ |