TES J-1200/30/VO
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w1D5DH_TES-J-1200-30-VO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: For 2-zone machines, the rear temperature is 450-520°F, and the front temperature is 420-470°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.060 | % | |
| 6.35 mm | 0.13 | % | |
| Water Absorption (24 hr) | 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 64 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 91.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7240 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 114 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 107 | °C | |
| 1.8 MPa, Unannealed | 101 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 221 to 238 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEDUR® L 9413-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| BITONER® BT-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Crastin® SK605 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| ICORENE® N9202 | ICO Polymers EMEA, A Division of A. Schulman | PET | ICORENE® |
| Plenco 01530 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |